PE flame retardant masterbatch LXM-PEM8007
In PE flame-retardant masterbatch formula, the halogen-free formula has good environmental protection, but there are some defects such as large addition amount, low flame retardant efficiency and great influence on PE products physical properties. Phosphate ester flame retardants, such as TPP, have a certain flame retardant effect, but these products are still limited in some areas. PE flame retardant masterbatch models are numerous, film type, pipe type, wire type, film type, casting film type, plastic pattern and V-0 no drip type, etc., suitable for LDPE,HDPE, the above models are based on bromo-antimony flame retardant compound, in line with ROSH, REACH requirements. Each type of formula, carrier, additives, etc. are different. The following to my factory production of LXM-PEM8007 wire type PE flame retardant masterbatch for introduction. If you inquire about other models, please contact us.
Ⅰ.Product Introduction
1. It has excellent antioxidant, acid and alkali resistance, weather resistance and high temperature resistance. 2. Extrusion sheet thickness uniform, no convex points, stable, holes and other phenomena.
3. Continuous production of non-stick roll, non-stick mold, no precipitation.
4. PE flame retardant masterbatch High strength, impact resistance, dust reduction, convenient transportation and storage.
5. Good dispersion, suitable for wire drawing, extrusion sheet, continuous wire, longtime without blocking the net.
6. Effectively improve the quality and appearance of PE products, high yield.
7. It has certain toughness, making PE products more convenient to process.
Ⅱ.Product indicators
Appearance: White granules
Flame retardant content >55%
Density: 1.393g/cm3
Melting finger: 12 (190 degrees /5 kg); 143 (190 degrees /21.6 kg)
Ⅲ.Field of application
Suitable for plastic, electronics, textile, paint, building materials, decorative materials, shoes and other composite products.
Ⅳ.Application data
Metrics | A | B | C | D |
LDPE2426H | 80 | - | ||
LLDPE1802 | 85 | 80 | ||
HDPE(5000S) | - | 80 | - | |
PEM8007 | 20 | 20 | 15 | 20 |
Flame retardant 0.8mm(once) | 2 seconds | 3 seconds | 3 seconds | 2 seconds |
Flame retardant 0.8mm(secondary) | 4 seconds | 4 seconds | 3 seconds | 4 seconds |
Flame retardant 1.6mm(once) | 1-3 seconds | 2-3 seconds | 3s | 1-3 seconds |
Flame retardant 1.6mm(secondary) | 1-3 seconds | 2-3 seconds | 3s | 1-3 seconds |
Flame retardant 3.2mm(once) | 1-3 seconds | 2-3 seconds | 3s | 1-3 seconds |
Flame retardant 3.2mm(secondary) | 1-3 seconds | 2-3 seconds | 3s | 1-3 seconds |
Ⅴ.Application Examples
PE extrusion bellows, HDPE23050 (60.8%) : LLDPE (15.2%) : PEM8007 Flame retardant masterbatch (22%) : black masterbatch (2%), out of fire.
Ⅵ.Instructions for use
PE flame retardant masterbatch LXM-PEM8007 can be directly measured and fed, but the recommended method is to mix with resin in an ordinary mixer and then carry out other processes.
Ⅶ.Packaging and Transportation
Packing shall be made of plastic and woven inside, stored in a cool and dry place, and transported according to non-dangerous goods.
PE flame retardant masterbatch LXM-PEM8007 granule uniform, easy to mix and feed, can effectively avoid dust pollution in the production process, in the use of the process basically no loss, thus reducing the consumption of raw materials, save production costs. It can be used with color masterbatch to prepare colored flame-retardant products. It also has the advantages of no precipitation, easy dispersion, high flame retardant efficiency, good whiteness and good plasticization.
PE flame retardant masterbatch